Buffing

The Base Metal has to be prepared by Buffing, Glazing and Polishing prior to being able to achieve good plating at lower thicknesses. The Ronuk Buffing Range encompasses the Conventional Buffing Compositions for different applications i.e. metals as well as plastics and ABS:

EMERY:

All meshes ranging from 60,90,120 to flour.

BRUSHING EMERY-BE:

For very rough mild steel components to be used on Belt or Fibre or Sisal.

BRUSHING EMERY:

For mild steel as above and can be used with R:30 or AT or RR to obtain superior finishs.

RONUK 30: (R:30)

R:30 is a popular product and usefull for Non-ferrous metals i.e. Gold, Silver, Copper and Brass and also usefull for ABS. In combination with Brushing Emery or RR for mild steel.

RONUK ‘AT’ SPECIAL:

For Aluminium, ABS and Zinc Die Castings.

RONUK ‘RR’ GREENISH ASH:

Stainless steel watch components and useful in combination with Brushing Emery or Mirror or Ronubuff RR.

RONUK PLASTIC NO. 1:

Plastic No. 1 is for final finishs of Plastic and Silver.

RONUK MIRROR:

Final finish of stainless steel with Ronusteel for Chrome Buffing or used alone. As the based metal merits.

RONUK RR BUFFING COMPOSITION (GREY):

For combinations with Brushing Emery specially for rims and cycle components.

RONUBUFF RR:

For Nickel and Chrome Burning useful after Hard Chrome Plating.

RONUBUFF BLUESTAR (BIG):

Useful for stainless steel in combination of Ronusteel and an alternative Peerless/Alps Polish for polishing of Mild steel, Copper, Brass and Nickel.

RONUBUFF BLUESTAR (SMALL):

For watch industry for finishingand glazing of stainless steel.

RONUBUFF-WHITE:

For Buffing of Hard Chrome and with combination of Mirror on Stainless Steel.

RONUKSTEEL:

For stainless steel. Can be used for final finish in combination with Mirror or for cutting/glazing with Ronubuff RR Grey and/or Brushing Emery.

LS-10 LIQUID/SOLID:

For Horn, Marble Plastic, Buttons, Spectacle frames and ABS $ and Methacrylate Bakelite components. Phenolic Moulding.

Description / Specification of Copper Plating Chemical

We are involved in offering a wide range of Copper Plating Chemical to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Copper Plating Chemical. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

NICKEL PLATING CHEMICALS:

Ronuk has developed new Nickel Plating Processes which has high leveling ability even at reduced Nickel thickness to balance the rising material cost and labour with a view to meeting the demands of our valued customers for better finish. Nickel/Chrome Plating is still the most widely used decorative electroplated finish on metals. 

a) DWA DUPLEX NICKEL :

This Duplex system provides semi bright sulphur free leveled nickel deposits with excellent mechanical and corrosion resistant properties and especially suitable for the rigours of a Duplex nickel system. Duplex coating of Nickel offers considerably higher corrosion resistance and durability, when applied on mild steel at lower thickness.

b) ECONIK: Duplex Nickel Process DWA – II :

Econik Duplex Nickel Process DWA-II produces non-glaring silky, Sulphur Free, attractive Leveled Nickel deposit for rack/Barrel plated parts. The added advantage of this system is that after Duplex Nickel the Dragout of Bright Nickel can be reused in semi Bright Bath resulting in a high level of economy to the user as close looped system is created due to the Brightners & Additives of Both Systems being Totally Compatible. 

MARINA NICKEL PROCESS :

A matt deposit of High Speed, easy to manage composition with good chrome receptivity. Large volumes of work and required deposition can be obtained with these salts.

NICKEL 103 SIXO PROCESS:

Most suitable for barrel plating. Can be operated at minimum 6 volts and is a highly conductive salt. 

NICKEL 104 TEVO PROCESS:

General purpose barrel plating salts for usage at 10V to 12 Volts.

NICKEL 101 OLSHO PROCESS:

Satisfactory Dull Nickel Salts for deeply recessed articles can be used at Room Temperature. Highly economic And useful for repair work and existing articles.

NI 105 AKNIK BLACK NICKEL PROCESS:

For Black Nickel Black on Brass, Copper and Mild Steel. It 9ives a lustrous Jet Black finish. It can be lacquered for longer life of the electroplate. 

AKNIK LIQUID REGENERATOR:

Used with the Nickel Aknik Black Nickel process for the better finish. 

CHELUX BRIGHT NICKEL SALTS:

These are proprietory Bright Nickel Salts of a high level purity compounded from Basic Salts manufactured by us.

CHELUX NICKEL BRIGHTNER: C.3:

Extremely white Mirror bright and brilliant finish can be obtained from this salt. Very tolerant to variation in 
temperature and tolerant to impurities. Suitable for manual and automatic vat and barrel installations to get uniform finishes. It has a ‘Lamellar’ crystal structure when used with our various Nickel Brightner systems. It is specially good as an undercoat to Gold and Silver and is used in combination with additives, 222 or C2 Processes. 

CHELUX BRIGHTENING AGENT C2 (SOLID):

The extremely ductile white Mirror finishes from C2 Solid are also produced from C2 (liquid) which has been developed for ease of use by our valued customers.

CHELUX LEVEL BRIGHTNER C2 (L):

Solid Brightner used with Chelux Bright Nickel Process to achieve brilliant and leveled Mirror Bright finish .

JAYLUX NICKEL BRIGHTNER:

Ronuk Brightner used with Chelux Bright Nickel Salts to achieve brilliant and white Mirror Bright finishes on metal. Can be used in combination with any of the Ronuk Additives like QBA-222 or C2 (Liquid or Solid).

QUICKBRITE NICKEL PROCESS: A-333 BRIGHTNER:

For Bright Nickel Plating very Quick Brightness can be achieved for a Thick or Thin Nickel layer and has all the necessary properties like Ductility, High Gloss, Leveling& consists the of A-333 & A-222. These Components are useful for general purpose requirements. This Process has excellent Versatility and a wide range of applications.

NIKBRITE 595: BRIGHT NICKEL PROCESS:

Versatile in operation with good Mechanical Properties & excellent Chrome Receptivity coupled with economical in use, making this combination popular with Job platers. 

A-222 NICKEL ADDITIVES ARE COMPATIBLE WITH ALL RONUK BRIGHTNERS.

LEVELLER 444:

Specially formulated for spokes & Rim plating in combination with C3-Chelux Nickel. Brightner
It increases Brightness & Leveling.

NICKEL ADDITIVE LLC-24:

Specially formulated for spokes & Rim plating in combination with C3-Chelux Nickel. Brightner
It increases Brightness & Leveling.

NICKEL LEVELLER-JAY-5

A composite liquid leveler for use in combination with Ronuk Bright Nickel Processes to obtain higher degree of leveling. in “STILL” or barrel lines. 

RONUK TRENIK PLATING PROCESS:

It is a Triplex Nickel Plating Process & imparts a Sulphur enriched layer between semi-bright & Bright Nickel Plating and ensures an additional safeguard against vertical corrosion & helps reduce to an extent nickel thickness when the 3 layers are plated in the correct percentages.

NICKEL ADDITIVE NICKEL 43:

Purifier for All Bright Nickel systems. Improves tolerance to Metallic impurities & whitens the electroplated layer & reduces “Down Time” by permitting tolerable plating although the Bath is infused with impurities.

ASTA NICKEL PURIFIER:

Solid purifier to be packed in filter with Carbon. Can be used with all bright Nickel systems to improve tolerance to organic and In-organic impurities. This product is normally prescribed for Preventive Maintenance.

RONUK ANTI STRESS AGENT: NICKEL ANTI-PITTING AMA:

Excellent for reducing Pitts and rectify imbalanced Stress and Strain is used for all Nickel solutions.

NICKEL ANTIPIT SB:

Used with RONUK Semi Bright & trenik Nickel solutions for reducing pitts.

SULPHAMATE NICKEL SOLUTION:

An almost Zero stress solution for ‘Electroforming’ Processes. ANTI PIT AMA can be used to advantage in this solution. 

SULPHAMATE NICKEL SOLUTION:

Extra pure Nickelsulphate, Nickel Chloride and Nickel Carbonates are manufactured by Ronuk. Use of these chemicals eliminates costly down time, high pH treatments and Electrolytic dummying. 

C5:

Low temperature Nickel Additive useful for Watts Bath & High chloride Baths. To be used with C3 or 333 or 595 Brightner. 

Description / Specification of Chrome Plating

We are involved in offering a wide range of Chrome Plating to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Chrome Plating. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

Description / Specification of Silver Plating

We are involved in offering a wide range of Silver Plating to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Silver Plating. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

ALKALINE NON CYANIDE ZINC-IRON PROCESS

FEZINK 206 is an alkaline zinc-iron electroplating process with good metal distribution properties, which adds to the traditional qualities of the FEZINK process the anti-corrosion properties and yellow and black finish requirements demanded by the automotive sector. In excess of 200 hours salt spray after thermal shock (1 hour at 120°C). 

MAKE-UP

• Fill the tank one third full with water, preferably Dl water.
• Add the required amount of sodium hydroxide bit-by-bit with vigorous mixing (the reaction is highly exothermic; ensure the tank lining can withstand the temperature reached).
• Dissolve the zinc metal required.
• Allow solution to cool to 30°C.
• Add FEZINK Purifier 0.5 – 1.0 ml/l
• Give Dummy to the solution for few hours.
• Add FEZINK Brightner at the rate of 8 – 10 ml/l
• Put the solution under continuous filtration.
• Add FEZINK 206 Complex at the rate of 75 ml/l.
• Add FEZINK 206 Iron Additive at the rate of 3.5 ml/l.
• Put the solution under continuous filtration for at least 4 – 6 hours.

MAKE-UP QUANTITIES

FOR RACK & BARREL	RANGE	OPTIMUM
CAUSTIC SODA	110 – 130 g/l	120 g/l
ZINC METAL (99.99 PURITY)	9 – 10 g/l	11 g/l
IRON	50 – 120 ppm	70 ppm
FEZINK 206 COMPLEX	70 – 80 ml/l	75 ml/l
FEZINK 206 PURIFIER	0.5 – 1.0 ml/l
FEZINK 206 BRIGHTNER	8 – 12 ml/l	10 ml/l

OPERATING CONDITIONS

	BARREL	RACK
TEMPERATURE	24 – 27ºC	24 – 27ºC
CATHODE CURRENT DENSITY	0.5 – 1.0 A/dm2	1 – 3 A/dm2
VOLTAGE	10 – 20 Volt	70 ppm
CURRENT LOADING A/LITR 0.7 MAXIMUM

REPLENISHMENT PER 10000 AHR (BOTH RACK AND BARREL)

FEZINK 206 Purifier – 2 litres FEZINK 206 Purifier per 50 kg of Sodium Hydroxide added
or 0.4 ml/l at each line start-up                                       
FEZINK 206 Brightner – 1 – 2 litres
FEZINK 206 Complex – 6 litres per 8 kg Sodium Hydroxide added
FEZINK 206 Iron Additive – 0.5 – 2 litres

CONTROLS OVER BATH CONSTITUENTS

Sodium Hydroxide        consumed through drag – out. Control through analysis
Zinc Metal                     Control through analysis

This concentration of zinc should be controlled by use of an appropriate ratio of soluble anode
(zinc) surface and insoluble anode (mild steel) surface. During period of no production, zinc in
contact with steel baskets dissolves and concentration in the bath increases, this dissolution
rate increases with concentration of sodium hydroxide. It is therefore essential to remove the
soluble anodes from the tank during stoppage period.

In large volume installation, this requirement may be avoided by the following method:
The working tank is equipped only with insoluble steel anodes, the necessary zinc dissolution to maintain electrolyte equilibrium is carried out in an auxiliary tank, connected to the working tank.

FEZINK 206 BRIGHTNER

This brings brightness to the deposit.  It need not be used if appearance requirements are not critical.

FEZINK 206 PURIFIER

This precipitates out metallic impurities which are inevitable in any treatment line. An excess is not harmful, but can turn the solution slightly cloudy.  In this case, an addition of up to 5 ml/l  bleach is required to produce a clear solution. Where the deposit at low cathode current densities is black, an addition of 2 – 4 ml/l FEZINK 206 Purifier will, in the majority of cases, cure this problem.

FEZINK 206 COMPLEX

This maintains iron in solution and prevents its precipitation.

FEZINK 206 IRON ADDITIVE

This additive contains iron. An addition of 0.35 ml/l increases the iron content of the bath by 10 ppm.

EQUIPMENT

All equipment must be thoroughly cleaned prior to use.

• Tank: Mild Steel or suitably lined.
• Anodes: It is recommended to use insoluble mild steel anodes of 3 -4 mm thickness to obtain a 1:1 anode / cathode ratio.  The metal concentration in solution is maintained through the dissolution of zinc balls, bars, ovals or plate anodes (99.99% pure)

contained in iron baskets.  Dissolution is encouraged if the steel surface area in contact with zinc is as large as possible (sand blast or shot blast steel).

• Agitation: Mechanical agitation is recommended. Air agitation is not desirable.
• Filtration: Continuous at the rate of 1-2 tank turn overs per hour.  Use Plate or cartridge filter of porosity 10µm optimal filtration is necessary to obtain full brightness; presence of suspended particles will lead to mat deposit and risk of blistering.
• Extraction: Desirable
• Heating and Cooling: Steel or titanium (24 – 40°C).

PROCESS SEQUENCE

The quality of deposit obtained depends upon the proposed pre-treatment sequence. Use on non-ionic surfactants is highly recommended throughout preparation sequence.
For steel, following sequence is recommended.
1. Immersion clean
2. Water rinse
3. Pickle
4. Water Rinse
5. Electro – clean
6. Water Rinse
7. Activation 
8. Water Rinse
9. Static Rinse prior to zinc plate
10. Zinc plate
11. Water rinse
12. TRIBLAK Passivation
13. Water rinse
14. Topcoat
15. Dry

HEALTH & SAFETY:

Keep containers tightly closed when not in use. Store in dry place and protect from dust.  Wear eye/face protection, gloves and protective clothing.  Avoid contact with eye and skin, in case of contact, wash with fresh water, and avoid breathing fumes, mist or sprays.

EFFLUENT TREATMENT

Mix vigorously and reduce the pH to 9.00 with dilute acid.  Filter out or clarify and decant off the precipice zinc. Adjust the pH of the filtrate according to local pollution control regulation before discharge.

DISCLAIMER

Our recommendations are made in good faith and are based on our skill and experience. As conditions of use are normally not in our control nor ideal. Ronuk does not give any guarantee or warrantee explicit or implicit and we are not liable to any person or corporate by reason thereof.

Description / Specification of Electro Polishing

We are involved in offering a wide range of Electro Polishing to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Electro Polishing. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

AURON PROCESS:

For maintainence to be used in Usex Brass salts to Impart a more golden shade.

RONUK BRASS BRIGHT BRONZE PROCESS:

Shades from Gold to Coppery Red by combining Usex copper and Brazin Zinc Salts.

BLACK BRONZE:

Shades of Black on copper and Brass and used to impart an antiquated work.

BROWN BRONZE:

Rich Brown to Chocolate on copper and Brass, used for figurines and watch dials

Antique Green on Brass- imparts an aging greenish look to figurines of copper, Brass work.
Antique Red on Brass- Imparts a Reddish look.
Antique Blue on Brass- Imparts a Blue Finish.

COPPER OXIDIDING LIQUID:

Helps impart various shades of gold to brown on copper and Brass. Used by Watch Dial manufacturers, Antique figures etc.

FERROPREP : AC (HEAVY DUTY ELECTROCLEANER FOR STEEL)

FERROPREP: AC is a highly conductive, alkaline, Heavy-Duty anodic for steel. 
In addition to its high capacity for removing a whole variety of soils, Ferroprep: AC is comparatively tolerant to both hard water and to hexavalent chromium. As a result Ferroprep: AC is especially recommended for use in areas where hard water may be encountered.
W hen used under the correct conditions, Ferroprep: AC will produce a bright smut free surface on the steel basis metal. However, as it has been designed for use with heavily soiled polished steel, especially when only light cleaning operations are required lower range of product could be used.

OPERATING CONDITIONS

  OPTIMUM RANGE
FERROPERP: AC 75 g/L 50-100 g/L
TEMPERATURE 90°C (190°F) 85-95°C (185-200°F)
CURRENT DENSITY 5-10 A/dm2 (50-100 A/ft.2) Room
TIME 1-5 minutes  
TANKS AND HEATERS Steel  
ELECTRODES Steel  

MAKEUP PROCEDURE

The tank should be 2/3 filled with water and heated to 60°C (140°F). The required quantity of Ferroprep: AC should then be slowly added with continuous stirring. When dissolved, adjust the solution to the desired volume and heat to the operating temperature.

WASTE DISPOSAL

Solutions of Ferroprep: AC are alkaline. Neutralize to pH 6-8 with an acid and discharge to sewer. Acid must be added slowly and with caution. Wear goggles and protective clothing.

CAUTION

Ferroprep: AC is highly alkaline. Protect eyes with goggles and wear protective clothing. Avoid eye and skin contact. Flush exposed areas immediately with cold water. Call a doctor in case of injury.

top
 

[/toggle]

Metaprep : HSC

METAPREP : HSC (MULTIPURPOSE ALKALINE HEAVY SOAK CLEANER)

Ronuk Metaprep H.S.C. is a high – efficiency, multipurpose alkaline heavy duty soak cleaner designed for use wherever a large variety of SOILS on metals must be processed. Oils, greases, waxy drawing compounds, buffing residues, sulphurized and chlorinated oils, and emulsion cleaner films are easily penetrated, softened and removed. The activity of the cleaners is accelerated with the use of air, mechanical or ultrasonic agitation. It has particularly good penetrating powers and is therefore suitable for tubular wire work.

OPERATING INFORMATION

For use on Mild Steel & Ferrous Metals

  OPTIMUM RANGE
RONUK METAPREP H.S.C. 60 g/L 40-75 g/L
TEMPERATURE 90°C (119°F) 85-95°C (185-200°F)
SOAK TIME 3 minutes 1-5 minutes
TANKS AND COILS Steels  
AGITATION Air preferred. Mechanical or ultrasonic can also be used.
OPTIMUM Air should be supplied from a filtered low pressure blower.

For use on Copper & Brass (Soak Only)

  OPTIMUM
RONUK METAPREP H.S.C. 50 g/L (40-70 g/L)
TEMPERATURE 65°C (60-70°C)
TIME 1-5 minutes
TANKS AND COILS Steels
AGITATION Air or Mechanical

MAKEUP PROCEDURE

Ronuk Metaprep HSC is dust-free, free flowing and soluble. The tank should be filled 3/4 full with water and warmed to 55-60°C (130-140°F). The required quantity of Ronuk Metaprep H.S.C. should then be slowly added with continuous stirring. After the powder has dissolved, adjust solution to the desired level with water and heat to operating temperature.
Can be used Electrolytically for steel only.

CURRENT DENSITY 2-4 amps / sq. dm.
TEMPERATURE 60-70°C

WASTE DISPOSAL

Ronuk Metaprep HSC solutions are alkaline. Neutralize pH 6 to 8 with an acid and discharge to sewer. The acid must be added slowly and with caution. Avoid eye or skin contact and wear protective clothing and safety goggles. 

CAUTION

Ronuk Metaprep H.S.C. is highly alkaline and can cause severe burns. Avoid contact with skin and eyes. Avoid inhaling powder. Wear protective clothing and safety goggles. Flush exposed areas with clean cold water. In case of injury consult doctor. 

Description / Specification of Pickling Chemicals

We are involved in offering a wide range of Pickling Chemicals to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Pickling Chemicals. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

RUSGARD 106 DW:

It is a rust preventive oil based on dewatering type. It is used for temporary protection of metal component. 

RUSGARD 16 DW:

It is also based on dewatering type having high viscosity and is used for some longer protection where the metal is to be used continuously. 

RUSGARD 17 ND:

It is drying type rust preventive oil with higher viscosity and good adhesion property on surface.

RUSGARD 18 DR:

It is drying type rust preventor having thick coating on metal surface and used for longer period on exposure to humid condition and air.

PHOSCOPASS:

It is a passivating chemical used after phosphating to seal the pores of the phosphate coating and gives it the corrosion resistance.
 

ZINCOPASS:

It is a chromium based passivating chemical for zinc phosphate process.
 

ZIRCOPASS:

It is a chromium free passivating chemical and meets the need for eco friendly product for chemically pre treating metallic surfaces. Zircopass can be applied by immersion or spraying.

PAINT REMOVERS:
PAINT-STRIP:

It is used for removing epoxy based paints and polyurethane within a short period of time. It is solvent based.
 

STRIP-101:

It is used for removing paints like epoxy base and other types i.e. on plastic components and as well as from metal components.

Description / Specification of Recycling Of Trivalent Chrome Passivation Bath

We are involved in offering a wide range of Recycling Of Trivalent Chrome Passivation Bath to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Recycling Of Trivalent Chrome Passivation Bath. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

Plant accessories

WATER SAVING AND RECYCLING SYSTEM

We specially design in Ion Exchange Systems for:

• Copper Nickel Chrome Recovery and Recycling of Rinse Water 
• Precious Metal Recovery 
• Trivalent Chrome Passivation Purification Units 
Read More

THE ENTIRE SPECTRUM OF ELECTROPLATING CONSUMABLES

Consult our catalog and find the entire spectrum of electroplating consumables.

Topics:

• Anode accessories (holders, baskets, linings, bags)
• Small electroplating devices (with/without workpiece baskets, plating drums, drum apparatuses, etc.)
• Centrifuges (drying centrifuges, spare parts)
• Electric accessories (bath heater, heating rods, floating switches, temperature sensors, etc.)
• Filter units (different type classes, spare parts, rotary pumps, filter cartridges, etc.)
• Oil strainers
• Diverse accessories (dosing devices and dosing pumps, barrel pumps, isolators, etc.)
• Electroplating/laboratory apparatus 

RONUK SUPPLY POWER SAVING EQUIPMENTS

• Hot Water Generator 
• VAM – Vapour Absorption Machine 
• HRU – Heat Recovery Unit 
• Heat Chill Pump 
• Cool Rectifiers

Description / Specification of Electroplating Plants

We are involved in offering a wide range of Electroplating Plants to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Electroplating Plants. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

Description / Specification of Anodizing Plants

We are involved in offering a wide range of Anodizing Plants to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Anodizing Plants. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

Description / Specification of Phosphating Plants

We are involved in offering a wide range of Phosphating Plants to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Phosphating Plants. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design 

 

Description / Specification of Effluent Treatment Plant

We are involved in offering a wide range of Effluent Treatment Plant to our most valued clients. Our range of these are widely appreciated by our clients which are situated all round the nation. We offer our range of it at most affordable prices.

We introduce ourselves as an eminent trader and supplier of an extensive array of  Effluent Treatment Plant. Prior to dispatch, our quality controllers run numerous tests on the entire range on various parameters of quality and durability. The offered equipment is manufactured using superior quality components with the aid of sophisticated techniques at the vendors' end. Moreover, our precious clients can purchase it in different technical specifications at reasonable price from us within promised time frame.
Features:

Sturdy design
Highly durable
Application specific design